PV1503大众汽车高温高压蒸汽油漆涂层喷射
changes the following changes have been made as compared to test specification pv 1503, 1998-02: standard compley revised contents of pv 1504 added
previous issues pv 1503: 1987-10; 1996-12; 1998-02; pv 1504: 1990-10
1 scope this standard describes a procedure to determine paint adhesion on metallic and non-metallic materials. it simulates the stresses produced when surfaces are cleaned with a steam jet using two different tests: test a: flat angle of jet along the two intersecting legs of the st. andrew's cross (see figure 1) test b: steep angle of jet in the center of the st. andrew's cross the test to be used shall be agreed with the responsible engineering department.
2 description steam jet test according to pv 1503a, or steam jet test according to pv 1503b.
3test method
3.1 equipment and auxiliary equipment steam jet (e.g. kärcher or nifab) painted non-metallic parts (e.g. bumper and mirror housing) painted metallic exterior parts and parts of the chassis scratch marker per van laar and clemen according to din en iso 7253cutter (e.g. edding, cutter ml 18)
3.2 specimen preparation
3.2.1 unloaded steam jet test (as-received condition) conditioning of painted plastic parts for 48 h at 50 °c or 24 h at 60 °c followed by aging in the din 50 014 – 23/50-2 standard climate. conditioning of painted metallic exterior parts and parts of the chassis for 24 h in the din 50 014 – 23/50-2 standard climate.
3.2.2 steam jet test after loading (e.g. 240 h according to din 50 017 kk) conditioning of the specimens before the steam jet test after loading (e.g. 240 h according to din 50 017 kk). acclimatization of the plastic parts for 24 h in the din 50 014 – 23/50-2 standard climate.
3.3 test conditions and setting parameters see table 1.
1 parameter pv1503a pv1503b
1 preset working pressure (depending on device type and hose length) (90 ± 5) bar
2 outlet temperature measured 10 cm from the nozzle (60 to 70) ℃
3 impact pressure measured 15 cm from the nozzle at an angle of 90° (19 ± 2) n
4 nozzle type depending on device manufacturer spraying systems tp2505 eg nifab 2506
5 distance from nozzle to specimen = 15 cm to be used for paint coatings of any type on plastic and metal on the exterior of the vehicle (requirements according to technical supply specification).
6 distance from nozzle to specimen = 5 cm to be used for low-temperature paint coating (e.g. 90 °c) on all substrates, see no. 12 for control limit, paint flakes
7 distance from nozzle to specimen = 2 cm to be used for high-temperature paint coating (140°c); control limitand requirement as for no. 6.
8 angle of jet 45° 90°
9 duration of spraying spraying acc. to figure 1 1 x 20 s, slight swinging movement, even spraying above the point of intersection of the st. andrew's cross.
10 nozzle alignment along the intersecting legs of the st. andrew's cross point of intersection of the st. andrew's cross on the specimen
11 spray pattern (check of the setting parameters) materialtobeused:styroformrtmfromstadur-südgmbh,procedureaccordingto3.4.1
12 control limit paint flakes ≥ 3 mm² and an acceptable test result at 15 cm (distance from nozzle to specimen) indicate a test result that is still acceptable. however, the paint adhesion of the specimen must be optimized and the specimen must be resubmitted.
3.4 procedure
3.4.1 check of the spray pattern the spray pattern is checked using an extruded polystyrene hard foam (see section 3.3, table 1, no. 11) with a closed cell structure and flame-retardant additive. the styroform block is placed in a clamp and the test is carried out with a distance of 12 cm between the nozzle and the block. the penetration depth of the spray jet shall not exceed 5 mm and the spray pattern length shall not exceed 10 cm.
3.4.2 procedure with specimens a crosscut (st. andrew's cross) is made in the specimen according to din en iso 7253 (the paint structure must be scribed down to the substrate). the specimen is then subjected to the steam jet under the conditions specified in section 3.3.
3.5 evaluation the specimen is visually inspected for any evidence of detachment of the paint surface after spraying with the steam jet. the evaluation is based on the degree of damage (length of the detached area at the st. andrew's cross in mm). minor flakes up to 1 mm caused by bad cutting at the crosscut will be disregarded from the evaluation.
4 referenced standards*)
din 50 014 climates and their technical application; standard atmospheres
din 50 017 atmospheres and their technical application; condensation water test atmospheres
din en iso 7253 paints and varnishes – determination of resistance to neutral salt spray (fog)
访客机品牌推荐
IGF-1 ELISA kit试剂盒
B1级橡塑,橡塑板制造商
贴标机的分类和应用
浙江混凝土表面为什么会出现色差材料
PV1503大众汽车高温高压蒸汽油漆涂层喷射
从水泥到焚烧，到环保新材料，跨界跨成海螺这样：毕业了
正确安装垃圾分类电子秤可帮助进行有效的垃圾分类
三辊卷板机的操作与保养规程详解
环氧陶瓷涂料使用范围
碳排放在线监测系统解决方案
皮肤病液氮容器冷冻疗法的生物学效应
E+H恩德斯豪斯音叉开关工作原理介绍
卧式螺带混合机选购注意点
数控系统的使用检查方法
供应天津永富牌醇酸调和漆,油漆,涂料
固体重金属捕捉剂 优势及特点
山西地区第三方检测低浓度采样头铝箔圈采购优惠价格
水家电“神奇功效”只是传说吗？
介绍zw32手动型真空开关和智能型看门狗开关外形尺寸图
previous issues pv 1503: 1987-10; 1996-12; 1998-02; pv 1504: 1990-10
1 scope this standard describes a procedure to determine paint adhesion on metallic and non-metallic materials. it simulates the stresses produced when surfaces are cleaned with a steam jet using two different tests: test a: flat angle of jet along the two intersecting legs of the st. andrew's cross (see figure 1) test b: steep angle of jet in the center of the st. andrew's cross the test to be used shall be agreed with the responsible engineering department.
2 description steam jet test according to pv 1503a, or steam jet test according to pv 1503b.
3test method
3.1 equipment and auxiliary equipment steam jet (e.g. kärcher or nifab) painted non-metallic parts (e.g. bumper and mirror housing) painted metallic exterior parts and parts of the chassis scratch marker per van laar and clemen according to din en iso 7253cutter (e.g. edding, cutter ml 18)
3.2 specimen preparation
3.2.1 unloaded steam jet test (as-received condition) conditioning of painted plastic parts for 48 h at 50 °c or 24 h at 60 °c followed by aging in the din 50 014 – 23/50-2 standard climate. conditioning of painted metallic exterior parts and parts of the chassis for 24 h in the din 50 014 – 23/50-2 standard climate.
3.2.2 steam jet test after loading (e.g. 240 h according to din 50 017 kk) conditioning of the specimens before the steam jet test after loading (e.g. 240 h according to din 50 017 kk). acclimatization of the plastic parts for 24 h in the din 50 014 – 23/50-2 standard climate.
3.3 test conditions and setting parameters see table 1.
1 parameter pv1503a pv1503b
1 preset working pressure (depending on device type and hose length) (90 ± 5) bar
2 outlet temperature measured 10 cm from the nozzle (60 to 70) ℃
3 impact pressure measured 15 cm from the nozzle at an angle of 90° (19 ± 2) n
4 nozzle type depending on device manufacturer spraying systems tp2505 eg nifab 2506
5 distance from nozzle to specimen = 15 cm to be used for paint coatings of any type on plastic and metal on the exterior of the vehicle (requirements according to technical supply specification).
6 distance from nozzle to specimen = 5 cm to be used for low-temperature paint coating (e.g. 90 °c) on all substrates, see no. 12 for control limit, paint flakes
7 distance from nozzle to specimen = 2 cm to be used for high-temperature paint coating (140°c); control limitand requirement as for no. 6.
8 angle of jet 45° 90°
9 duration of spraying spraying acc. to figure 1 1 x 20 s, slight swinging movement, even spraying above the point of intersection of the st. andrew's cross.
10 nozzle alignment along the intersecting legs of the st. andrew's cross point of intersection of the st. andrew's cross on the specimen
11 spray pattern (check of the setting parameters) materialtobeused:styroformrtmfromstadur-südgmbh,procedureaccordingto3.4.1
12 control limit paint flakes ≥ 3 mm² and an acceptable test result at 15 cm (distance from nozzle to specimen) indicate a test result that is still acceptable. however, the paint adhesion of the specimen must be optimized and the specimen must be resubmitted.
3.4 procedure
3.4.1 check of the spray pattern the spray pattern is checked using an extruded polystyrene hard foam (see section 3.3, table 1, no. 11) with a closed cell structure and flame-retardant additive. the styroform block is placed in a clamp and the test is carried out with a distance of 12 cm between the nozzle and the block. the penetration depth of the spray jet shall not exceed 5 mm and the spray pattern length shall not exceed 10 cm.
3.4.2 procedure with specimens a crosscut (st. andrew's cross) is made in the specimen according to din en iso 7253 (the paint structure must be scribed down to the substrate). the specimen is then subjected to the steam jet under the conditions specified in section 3.3.
3.5 evaluation the specimen is visually inspected for any evidence of detachment of the paint surface after spraying with the steam jet. the evaluation is based on the degree of damage (length of the detached area at the st. andrew's cross in mm). minor flakes up to 1 mm caused by bad cutting at the crosscut will be disregarded from the evaluation.
4 referenced standards*)
din 50 014 climates and their technical application; standard atmospheres
din 50 017 atmospheres and their technical application; condensation water test atmospheres
din en iso 7253 paints and varnishes – determination of resistance to neutral salt spray (fog)
访客机品牌推荐
IGF-1 ELISA kit试剂盒
B1级橡塑,橡塑板制造商
贴标机的分类和应用
浙江混凝土表面为什么会出现色差材料
PV1503大众汽车高温高压蒸汽油漆涂层喷射
从水泥到焚烧，到环保新材料，跨界跨成海螺这样：毕业了
正确安装垃圾分类电子秤可帮助进行有效的垃圾分类
三辊卷板机的操作与保养规程详解
环氧陶瓷涂料使用范围
碳排放在线监测系统解决方案
皮肤病液氮容器冷冻疗法的生物学效应
E+H恩德斯豪斯音叉开关工作原理介绍
卧式螺带混合机选购注意点
数控系统的使用检查方法
供应天津永富牌醇酸调和漆,油漆,涂料
固体重金属捕捉剂 优势及特点
山西地区第三方检测低浓度采样头铝箔圈采购优惠价格
水家电“神奇功效”只是传说吗？
介绍zw32手动型真空开关和智能型看门狗开关外形尺寸图